- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.96
- 缺口冲击强度: 0.352
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 1.80
- 硬度: 95.0
- 热变形温度 [℃]: 112.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched | 0.352 J/cm | 0.660 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |