- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.96
- 缺口冲击强度: 1.17
- 拉伸强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 1.100
- 硬度: 61.0
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 61 | 61 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.350 GPa | 195.8 ksi | ASTM D638 |
| Flexural Strength | 24.0 MPa | 3480 psi | ASTM D790 |
| Flexural Modulus | 1.100 GPa | 159.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | |