- 密度 [g/cm3]: 1.68
- 缺口冲击强度: 2.3
- 拉伸强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 4.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Filler Content | 70 % | 70 % | ISO 3451 / 1 |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | ISO 868 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Elongation at Yield | 1.7 % | 1.7 % | ISO 527 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.30 kJ/m² | 1.09 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 |
| Vicat Softening Point | 120 °C | 248 °F | 49 N; ISO 306 |