- 熔体流动速率 [g/10min]: 21.0
- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 0.278
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 3.099
- 硬度: 83.0
- 热变形温度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 83 | 83 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.099 GPa | 449.5 ksi | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 3.099 GPa | 449.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.278 J/cm | 0.520 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | |