- 密度 [g/cm3]: 0.902
- 拉伸强度 [MPa]: 24.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.5 MPa | 3550 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min |
| Tensile Modulus | 1.18 GPa | 171 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 0.750 J/cm² | 3.57 ft-lb/in² | |
| 0.360 J/cm² @Temperature -30.0 °C | 1.71 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 163 °C | 325 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | |
| Vicat Softening Point | 71.0 °C | 160 °F | 50°C/hr; 50N |