- 密度 [g/cm3]: 1.5
- 缺口冲击强度: 2.5
- 拉伸强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 4.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Filler Content | 60 % | 60 % | ISO 3451 / 1 |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 86 | 86 | ISO 868 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Vicat Softening Point | 101 °C | 214 °F | 49 N; ISO 306 |