- 密度 [g/cm3]: 0.9
- 拉伸强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Index of Compound | 4.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 620 % | 620 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 152 °C | 306 °F | DSC |
| Vicat Softening Point | 123 °C | 253 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 230 °C | 446 °F | |
| Adapter Temperature | 230 °C | 446 °F | |
| Die Temperature | 230 °C | 446 °F | |