- 密度 [g/cm3]: 0.89
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.580
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc @Temperature 23.0 °C | 0.0322 lb/in³ @Temperature 73.4 °F | ISO 1183 |
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO R 527 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| Flexural Modulus | 0.580 GPa | 84.1 ksi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 151 °C | 304 °F | DSC |
| Vicat Softening Point | 122 °C @Load 0.999 kg | 252 °F @Load 2.20 lb | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 170 - 190 °C | 338 - 374 °F | |
| Zone 2 | 180 - 200 °C | 356 - 392 °F | |
| Zone 3 | 190 - 210 °C | 374 - 410 °F | |
| Zone 4 | 200 - 220 °C | 392 - 428 °F | |
| Die Temperature | 220 - 240 °C | 428 - 464 °F | |