- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 0.48
- 弯曲强度 [MPa]: 74.0
- 弯曲模量 [MPa]: 7.80
- 硬度: 105.0
- 热变形温度 [℃]: 167.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Ultimate | 74.0 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm | 4.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 167 °C | 333 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |