- 密度 [g/cm3]: 1.05
- 缺口冲击强度: 0.43
- 弯曲强度 [MPa]: 19.0
- 弯曲模量 [MPa]: 1.30
- 硬度: 90.0
- 热变形温度 [℃]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 289 % | 289 % | ASTM D638 |
| Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.3 J/cm | 19.3 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |