- 密度 [g/cm3]: 0.94
- 缺口冲击强度: 0.75
- 弯曲强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 1.10
- 硬度: 90.0
- 热变形温度 [℃]: 93.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 390 % | 390 % | ASTM D638 |
| Flexural Strength | 33.0 MPa | 4790 psi | ASTM D790 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 195 °C | 340 - 383 °F | Approximate middle barrel temperature range |