- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 0.8
- 弯曲强度 [MPa]: 77.0
- 弯曲模量 [MPa]: 5.90
- 硬度: 103.0
- 热变形温度 [℃]: 161.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |