- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C | 221 °F | 0.030 inch sample |
| Flammability, UL94 | V-0 @Thickness 0.810 mm | V-0 @Thickness 0.0319 in | |
| V-0 @Thickness 1.57 mm | V-0 @Thickness 0.0618 in | ||
| V-0 @Thickness 3.05 mm | V-0 @Thickness 0.120 in | ||