- 密度 [g/cm3]: 1.36
- 缺口冲击强度: 0.32
- 弯曲强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 2.70
- 硬度: 96.0
- 热变形温度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 - 221 °C | 410 - 430 °F | Approximate middle barrel temperature range |