- 缺口冲击强度: 0.69
- 拉伸强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 4.231
- 硬度: 107.0
- 热变形温度 [℃]: 159.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Index of Compound | 4.0 - 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.0 - 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 4.231 GPa | 613.7 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.86 J/cm | 9.10 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C | 232 °F | ASTM D648 |