- 熔体流动速率 [g/10min]: 12.0
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 4.27
- 硬度: 97.0
- 热变形温度 [℃]: 145.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Melt Flow | 12 g/10 min @Temperature 230 °C | 12 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Strength | 39.3 MPa | 5700 psi | ASTM D790 |
| Flexural Modulus | 4.27 GPa | 620 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| 0.214 J/cm @Temperature -30.0 °C | 0.400 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |