- 熔体流动速率 [g/10min]: 0.75
- 缺口冲击强度: 2.83
- 拉伸强度 [MPa]: 26.37
- 弯曲模量 [MPa]: 1.68
- 硬度: 80.0
- 热变形温度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.957 g/cc | 0.957 g/cc | ASTM D792 |
| Melt Flow | 0.75 g/10 min @Temperature 230 °C | 0.75 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 26.37 MPa | 3825 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 13 % | 13 % | ASTM D638 |
| Flexural Strength | 35.54 MPa | 5155 psi | ASTM D790 |
| Flexural Modulus | 1.68 GPa | 244 ksi | ASTM D790 |
| 2.20 GPa | 319 ksi | 1.3 mm/min; ASTM D790 | |
| Izod Impact, Notched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | ASTM D648 |