A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer

A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer 物性表: A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer物性表及特性介绍,A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer注塑参数详情,如需A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 9.0
  • 缺口冲击强度: 0.149
  • 拉伸强度 [MPa]: 26.2
  • 弯曲模量 [MPa]: 2.84
  • 热变形温度 [℃]: 115.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.10 - 1.16 g/cc1.10 - 1.16 g/ccASTM D792
Melt Flow 9.0 - 14 g/10 min
@Temperature 230 °C
9.0 - 14 g/10 min
@Temperature 446 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R >= 88>= 88ASTM D785
Tensile Strength, Yield >= 26.2 MPa>= 3800 psi2 in/min; ASTM D638
Elongation at Break >= 3.0 %>= 3.0 %ASTM D638
Flexural Modulus >= 2.84 GPa>= 412 ksiASTM D790
Izod Impact, Notched 0.149 J/cm0.280 ft-lb/inASTM D256
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) >= 115 °C>= 239 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) >= 80.0 °C>= 176 °FASTM D648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31170.html

免责声明: 本文 A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4