- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 2.67
- 拉伸强度 [MPa]: 17.9
- 弯曲模量 [MPa]: 1.34
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | at max load, 2 in/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Strength | 24.1 MPa | 3500 psi | ASTM D790 |
| Flexural Modulus | 1.34 GPa | 195 ksi | 1% secant; ASTM D790 |
| 1.53 GPa | 222 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | ASTM D648 |