- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 2.65
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 2.89
- 硬度: 69.0
- 热变形温度 [℃]: 117.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 69 | 69 | ASTM D785 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Flexural Modulus | 2.89 GPa | 419 ksi | ASTM D790 |
| Izod Impact, Notched | 2.65 J/cm | 4.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 243 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |