- 熔体流动速率 [g/10min]: 30.0
- 缺口冲击强度: 0.67
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.275
- 硬度: 88.0
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 30 g/10 min @Temperature 230 °C | 30 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Yield | 20 % | 20 % | ASTM D638 |
| Flexural Modulus | 1.275 GPa | 184.9 ksi | ASTM D790 |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 4.98 J | 3.67 ft-lb | -30°C; GM9300P |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |