- 熔体流动速率 [g/10min]: 29.0
- 缺口冲击强度: 1.25
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.266
- 热变形温度 [℃]: 119.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 29 g/10 min @Load 2.16 kg, Temperature 230 °C | 29 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
| Elongation at Break | 111 % | 111 % | at 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.266 GPa | 183.6 ksi | at 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.25 J/cm | 2.34 ft-lb/in | ASTM D256 |
| Gardner Impact | 31.0 J | 22.9 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ASTM D648 |