- 熔体流动速率 [g/10min]: 1.8
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.07
- 硬度: 80.0
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | at max load; ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | at 0°F; ASTM D256 |
| 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 | |
| Gardner Impact | >= 10.2 J | >= 7.50 ft-lb | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |