- 熔体流动速率 [g/10min]: 6.0
- 缺口冲击强度: 1.34
- 拉伸强度 [MPa]: 28.5
- 弯曲模量 [MPa]: 1.13
- 硬度: 80.0
- 热变形温度 [℃]: 87.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.912 g/cc | 0.912 g/cc | ASTM D792 |
| Melt Flow | 6.0 - 12 g/10 min @Temperature 230 °C | 6.0 - 12 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 28.5 MPa | 4130 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | >= 40 % | >= 40 % | at 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.13 GPa | 164 ksi | ASTM D790 |
| Izod Impact, Notched | 1.34 J/cm | 2.51 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Gardner Impact | 8.00 J @Temperature -30.0 °C | 5.90 ft-lb @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ASTM D648 |