- 熔体流动速率 [g/10min]: 6.0
- 吸水率 [%]: 0.03
- 缺口冲击强度: 1.33
- 拉伸强度 [MPa]: 27.2
- 弯曲模量 [MPa]: 1.14
- 硬度: 75.0
- 热变形温度 [℃]: 90.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C | 6.0 - 10 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 75 | 75 | ASTM D785 |
| Tensile Strength, Yield | 27.2 MPa | 3950 psi | ASTM D638 |
| Elongation at Break | 85 % | 85 % | ASTM D638 |
| Flexural Modulus | 1.14 GPa | 165 ksi | ASTM D790 |
| Flexural Stiffness | 931 MPa | 135000 psi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.6 °C | 195 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |