- 熔体流动速率 [g/10min]: 4.0
- 缺口冲击强度: 16.0
- 拉伸强度 [MPa]: 25.9
- 弯曲模量 [MPa]: 1.14
- 硬度: 70.0
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.902 g/cc | 0.902 g/cc | ASTM D792 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 25.9 MPa | 3750 psi | at 2 in/min; ASTM D638 |
| Elongation at Yield | 15 % | 15 % | ASTM D638 |
| Flexural Modulus | 1.14 GPa | 165 ksi | ASTM D790 |
| Izod Impact, Notched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Gardner Impact | 22.71 J | 16.75 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |