- 弯曲强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 0.0260
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | 15 sec delay; ASTM D2240 |
| Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
| Elongation at Break | 900 % | 900 % | 20 in/min; ASTM D412 |
| Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
| Tear Strength | 67.0 kN/m | 382 pli | 2 in/min; ASTM D624 |
| Compression Set | 23 % | 23 % | Method B, 22 h, 23°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 78.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 43.3 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM E831 |