- 缺口冲击强度: 1.87
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.10
- 热变形温度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Index of Compound | 10 g/10 min @Temperature 230 °C | 10 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 200 % | 200 % | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | 0.05 in.min, tangent; ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm | 3.50 ft-lb/in | ASTM D256 |
| Gardner Impact | 28.24 J | 20.83 ft-lb | ASTM D5420 |
| 22.60 J @Temperature -30.0 °C | 16.67 ft-lb @Temperature -22.0 °F | ASTM D5420 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |