- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 0.902
- 拉伸强度 [MPa]: 25.0
- 硬度: 86.0
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C | 13 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 86 | 86 | ISO 2039-2 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.25 GPa | 181 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| 0.400 J/cm² @Temperature -20.0 °C | 1.90 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Impact Test | 25.0 J | 18.4 ft-lb | Instrumental Falling Weight - Total Penetration Energy at -20°C; ISO 6603-2 |
| 35.0 J | 25.8 ft-lb | Instrumental Falling Weight - Total Penetration Energy at 0°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-2 |