- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.9
- 缺口冲击强度: 59.0
- 拉伸强度 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ISO 868 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 0.800 GPa | 116 ksi | At 1 mm/min; ISO 527-2 |
| Izod Impact, Notched (ISO) | 59.0 kJ/m² | 28.1 ft-lb/in² | ISO 108/1A |
| 10.0 kJ/m² @Temperature -20.0 °C | 4.76 ft-lb/in² @Temperature -4.00 °F | ISO 108/1A | |
| Peel Strength | 4.00 kN/m | 22.8 pli | 3 layer at 110°C; DIN 30678 |
| >= 20.0 kN/m | >= 114 pli | 3-layer; DIN 30678 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 130 °C | 266 °F | A50 (10 N); ISO 306 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Die Temperature | 235 - 245 °C | 455 - 473 °F | |
| Head Temperature | 235 - 245 °C | 455 - 473 °F | |