- 熔体流动速率 [g/10min]: 17.0
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 16.0
- 弯曲模量 [MPa]: 1.20
- 热变形温度 [℃]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | Borealis Method |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C | 17 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 400 % | 400 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.20 GPa | 174 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Strength | 22.0 MPa | 3190 psi | ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |
| 0.600 J/cm² @Temperature -20.0 °C | 2.86 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ISO 75-2 |
| Vicat Softening Point | 42.0 °C | 108 °F | B (50N); ISO 306 |
| 115 °C | 239 °F | A (10N); ISO 306 | |
| Shrinkage | 0.15 % | 0.15 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |