- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.04
- 拉伸强度 [MPa]: 20.99
- 弯曲模量 [MPa]: 2.10
- 热变形温度 [℃]: 98.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Borealis Method | ||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 30 g/10 min @Load 5.00 kg, Temperature 230 °C | 30 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 57.0 MPa | 8270 psi | H385/30; ISO 2039 | ||
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | At 50 mm/min; ISO 527-2 | ||
| Flexural Modulus | 2.10 GPa | 305 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 5.30 J/cm² @Temperature -20.0 °C | 25.2 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179/1eA | ||
| 0.300 J/cm² @Temperature -20.0 °C | 1.43 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ISO 75-2 | ||
| Vicat Softening Point | 56.0 °C | 133 °F | B (50N); ISO 306 | ||
| 132 °C | 270 °F | A (10N); ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 25 | VDA 277 | |||
| Fogging % | 97.4 | At 100°C/3 hours | |||
| Fogging, mg | 1 | At 100°C/ 16 hours | |||