- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.91
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.45
- 热变形温度 [℃]: 96.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 230 °C | 50 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 35.00 MPa | 5076 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 9.0 % | 9.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.55 GPa | 225 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.45 GPa | 210 ksi | At 5 mm/min; ISO 178 |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/1eU |
| 1.20 J/cm² @Temperature -20.0 °C | 5.71 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 |
| Vicat Softening Point | 92.0 °C | 198 °F | B (50N); ISO 306 |
| 153 °C | 307 °F | A (10N); ISO 306 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |