- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 0.905
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.50
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 | ||
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C | 14 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 62.0 MPa | 8990 psi | H 385/30; ISO 2039 | ||
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | At 50 mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.50 GPa | 218 ksi | At 1 mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 11.0 J/cm² | 52.4 ft-lb/in² | ISO 179/1eU | ||
| 6.20 J/cm² @Temperature -20.0 °C | 29.5 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA | ||
| 0.450 J/cm² @Temperature -20.0 °C | 2.14 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75-2 | ||
| Vicat Softening Point | 72.0 °C | 162 °F | B (50N); ISO 306 | ||
| 150 °C | 302 °F | A (10N); ISO 306 | |||
| Shrinkage | 1.5 % | 1.5 % | Borealis Method | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | Polymer Mass Temp | ||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 30 | VDA 277 | |||
| Fogging, mg | 1.4 | At 100°C/ 16 hours | |||