- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.9
- 弯曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 600 - 800 % | 600 - 800 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 - 800 % | 600 - 800 % | ISO 527-3 |
| Tensile Modulus | 0.450 - 0.550 GPa | 65.3 - 79.8 ksi | ISO 527-2 |
| Flexural Modulus | 1.10 GPa | 160 ksi | 50% relative humidity; ISO 178 |
| Dart Drop, Total Energy | 23.0 J @Thickness 0.0500 mm | 17.0 ft-lb @Thickness 0.00197 in | 1100; ISO 7765-2 |
| Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 158 - 162 °C | 316 - 324 °F | DSC; ISO 3146 |
| Vicat Softening Point | 147 °C @Load 1.02 kg | 297 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 40 % | <= 40 % | ASTM D1003 |
| Gloss | >= 3.0 % | >= 3.0 % | 60° of arc; ASTM D 2457 |