- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.55
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C | 13 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 57 g/10 min @Load 5.00 kg, Temperature 230 °C | 57 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 62.0 MPa | 8990 psi | H 385/30; ISO 2039 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.55 GPa | 225 ksi | At 5 mm/min; ISO 178 |
| Charpy Impact Unnotched | 5.10 J/cm² @Temperature -20.0 °C | 24.3 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| 0.360 J/cm² @Temperature -20.0 °C | 1.71 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75-2 |
| Vicat Softening Point | 70.0 °C | 158 °F | B (50N); ISO 306 |
| 150 °C | 302 °F | A (10N); ISO 306 | |
| Shrinkage | 1.5 % | 1.5 % | Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |