- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.905
- 弯曲模量 [MPa]: 0.550
- 热变形温度 [℃]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Slip Level | 2000 ppm | 2000 ppm | EAA; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Modulus | 0.300 GPa | 43.5 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 0.550 GPa | 79.8 ksi | ISO 178 |
| Dart Drop, Total Energy | 30.0 J | 22.1 ft-lb | 900N; ISO 7765-2 |
| Coefficient of Friction | >= 0.20 | >= 0.20 | ISO 8295 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 137 °C | 279 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ISO 75-2 |
| Vicat Softening Point | 116 °C @Load 1.02 kg | 241 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.5 % | <= 1.5 % | ASTM D1003 |
| Gloss | 135 % | 135 % | 20° of arc; ASTM D2457 |
| Component Elements Properties | Metric | English | Comments |
| SiO2 | 0.18 % | 0.18 % | Antiblock; Borealis Method |