Borealis EE002AE Polypropylene Elastomer Modified

Borealis EE002AE Polypropylene Elastomer Modified 物性表: Borealis EE002AE Polypropylene Elastomer Modified物性表及特性介绍,Borealis EE002AE Polypropylene Elastomer Modified注塑参数详情,如需Borealis EE002AE Polypropylene Elastomer Modified下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 11.0
  • 密度 [g/cm3]: 0.905
  • 缺口冲击强度: 12.0
  • 拉伸强度 [MPa]: 19.0
  • 弯曲模量 [MPa]: 0.900
  • 热变形温度 [℃]: 75.0
 
Physical PropertiesMetricEnglishComments
Density 0.905 g/cc0.0327 lb/in³ISO 1183
Linear Mold Shrinkage 0.0015 cm/cm0.0015 in/inpost shrinkage (2h/90°C)
 0.014 cm/cm0.014 in/inmold average
Melt Flow 11 g/10 min
@Load 2.16 kg,
Temperature 230 °C
11 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 5555ISO 868
Ball Indentation Hardness 36.0 MPa5220 psi132N/10s; ISO 2039
Tensile Strength, Yield 19.0 MPa2760 psi50mm/min; ISO 527-2
Elongation at Break >= 150 %>= 150 %50mm/min; ISO 527-2
Elongation at Yield 5.5 %5.5 %50mm/min; ISO 527-2
Tensile Modulus 0.950 GPa138 ksi1mm/min; ISO 527-2
Flexural Strength 21.0 MPa3050 psiISO 178
Flexural Modulus 0.900 GPa131 ksi2mm/min; ISO 178
Izod Impact, Notched (ISO)  12.0 kJ/m²
@Temperature -20.0 °C
5.71 ft-lb/in²
@Temperature -4.00 °F
ISO 180/1A
 57.0 kJ/m²
@Temperature 23.0 °C
27.1 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched  NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
ISO 179/1eU
 NB
@Temperature -20.0 °C
NB
@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm²
@Temperature -30.0 °C
3.33 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
 0.850 J/cm²
@Temperature -20.0 °C
4.04 ft-lb/in²
@Temperature -4.00 °F
ISO 179/1eA
 7.00 J/cm²
@Temperature 23.0 °C
33.3 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
CTE, linear 100 µm/m-°C55.6 µin/in-°F(-30°C/80°C); Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C167 °FISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C118 °FISO 75-2
Vicat Softening Point  45.0 °C
@Load 5.10 kg
113 °F
@Load 11.2 lb
ISO 306
 135 °C
@Load 1.02 kg
275 °F
@Load 2.25 lb
ISO 306
 
Processing PropertiesMetricEnglishComments
Processing Temperature 220 - 260 °C428 - 500 °Fmass temperature
Feed Temperature 40.0 - 80.0 °C104 - 176 °F
Mold Temperature 30.0 - 50.0 °C86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa4350 - 8700 psi
 
Descriptive Properties
Back Pressurelow to medium
Screw Speedlow to medium

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31563.html

免责声明: 本文 Borealis EE002AE Polypropylene Elastomer Modified 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4