- 熔体流动速率 [g/10min]: 70.0
- 密度 [g/cm3]: 0.903
- 拉伸强度 [MPa]: 25.0
- 硬度: 86.0
- 热变形温度 [℃]: 102.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.903 g/cc | 0.0326 lb/in³ | ISO 1183 | ||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C | 70 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 86 | 86 | ISO 2039-2 | ||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.45 GPa | 210 ksi | ISO 527-2 | ||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C | 1.90 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.550 J/cm² @Temperature 23.0 °C | 2.62 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | |||
| Descriptive Properties | |||||
| Injection Velocity | high | ||||