Borealis Daplen™ EF267AI Polypropylene TPO Compound

Borealis Daplen™ EF267AI Polypropylene TPO Compound 物性表: Borealis Daplen™ EF267AI Polypropylene TPO Compound物性表及特性介绍,Borealis Daplen™ EF267AI Polypropylene TPO Compound注塑参数详情,如需Borealis Daplen™ EF267AI Polypropylene TPO Compound下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 16.0
  • 密度 [g/cm3]: 1.04
  • 缺口冲击强度: 2.6
  • 拉伸强度 [MPa]: 27.0
  • 弯曲模量 [MPa]: 2.50
  • 热变形温度 [℃]: 105.0
 
Physical PropertiesMetricEnglishComments
Density 1.04 g/cc0.0376 lb/in³ISO 1183
Linear Mold Shrinkage 0.011 cm/cm0.011 in/inmold average;Borealis Method
Melt Flow 16 g/10 min
@Load 2.16 kg,
Temperature 230 °C
16 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Ball Indentation Hardness 61.0 MPa8850 psiH 358/30; ISO 2039
Tensile Strength at Break 10.0 MPa1450 psiISO 527-2
Tensile Strength, Yield 27.0 MPa3920 psi50mm/min; ISO 527-2
Elongation at Break 5.3 %5.3 %flexural strain; ISO 178
 15 %15 %ISO 527-2
Elongation at Yield 4.0 %4.0 %50mm/min; ISO 527-2
Tensile Modulus 2.45 GPa355 ksi1mm/min; ISO 527-2
Flexural Strength 36.0 MPa5220 psi3.5% strain; ISO 178
 38.0 MPa5510 psiISO 178
Flexural Modulus 2.50 GPa363 ksi2mm/min; ISO 178
Izod Impact, Notched (ISO)  2.60 kJ/m²
@Temperature -20.0 °C
1.24 ft-lb/in²
@Temperature -4.00 °F
ISO 180/1A
 6.40 kJ/m²
@Temperature 23.0 °C
3.05 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO)  27.0 kJ/m²
@Temperature -20.0 °C
12.8 ft-lb/in²
@Temperature -4.00 °F
ISO 180/1U
 93.0 kJ/m²
@Temperature 23.0 °C
44.3 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm²
@Temperature -20.0 °C
19.0 ft-lb/in²
@Temperature -4.00 °F
ISO 179/1eU
 12.0 J/cm²
@Temperature 23.0 °C
57.1 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched  0.280 J/cm²
@Temperature -20.0 °C
1.33 ft-lb/in²
@Temperature -4.00 °F
ISO 179/1eA
 0.650 J/cm²
@Temperature 23.0 °C
3.09 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
CTE, linear 55.0 µm/m-°C30.6 µin/in-°F(-30°C/80°C); Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 105 °C221 °FISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 56.0 °C133 °FISO 75-2
Vicat Softening Point  67.0 °C
@Load 5.10 kg
153 °F
@Load 11.2 lb
ISO 306
 141 °C
@Load 1.02 kg
286 °F
@Load 2.25 lb
ISO 306
 
Processing PropertiesMetricEnglishComments
Processing Temperature 220 - 260 °C428 - 500 °Fmass temperature
Feed Temperature 40.0 - 80.0 °C104 - 176 °F
Mold Temperature 30.0 - 50.0 °C86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec3.94 - 7.87 in/sec
Hold Pressure 3.00 - 6.00 MPa435 - 870 psi
 
Descriptive Properties
Back Pressurelow to medium
Emission (µgC/g)< 50VDA 277
Fogging (mg)< 2DIN 75201;100°C, 16h
Screw Speedlow to medium

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31577.html

免责声明: 本文 Borealis Daplen™ EF267AI Polypropylene TPO Compound 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4