- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.905
- 弯曲模量 [MPa]: 1.00
- 热变形温度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | base resin; ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Modulus | 0.550 GPa | 79.8 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 1.00 GPa | 145 ksi | 50% humidity; ISO 178 |
| Dart Drop, Total Energy | 17.0 J @Thickness 0.0500 mm | 12.5 ft-lb @Thickness 0.00197 in | 1000N; ISO 4465-2 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 150 °C | 302 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Vicat Softening Point | 139 °C @Load 1.02 kg | 282 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 2.0 % | <= 2.0 % | ASTM D1003 |
| Gloss | >= 130 % | >= 130 % | 20° of arc; ASTM D2457 |