- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.04
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 1.80
- 热变形温度 [℃]: 93.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | Borealis Method; anisotropic shrinkage | ||
| 0.0070 cm/cm | 0.0070 in/in | Borealis Method; isotropic shrinkage | |||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 35.0 MPa | 5080 psi | H 358/30 | ||
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.2 % | 5.2 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.75 GPa | 254 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.80 GPa | 261 ksi | 2mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -20.0 °C | 33.3 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -20.0 °C | 1.19 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | ||
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 | ||
| Vicat Softening Point | 49.0 °C @Load 5.10 kg | 120 °F @Load 11.2 lb | ISO 306 | ||
| 126 °C @Load 1.02 kg | 259 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 3.00 - 6.00 MPa | 435 - 870 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (µgC/g) | < 50 | VDA 277 | |||
| Fogging (mg) | < 2 | DIN 75201; 100°C, 16h | |||
| Screw Speed | low to medium | ||||