- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 97.0
- 弯曲模量 [MPa]: 6.20
- 热变形温度 [℃]: 159.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | average process; in flow; 150x80x2mm | ||
| 0.010 cm/cm | 0.010 in/in | average process; cross flow; 150x80x2mm | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 124 MPa | 18000 psi | 132 N/10s; ISO 2039 | ||
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | ISO 527-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 2.8 % | 2.8 % | ISO 527-2 | ||
| Tensile Modulus | 6.80 GPa | 986 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 | ||
| Flexural Modulus | 6.20 GPa | 899 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -20.0 °C | 3.81 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | ||
| 11.0 kJ/m² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU | ||
| 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.900 J/cm² @Temperature -20.0 °C | 4.28 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75-2 | ||
| Vicat Softening Point | 135 °C @Load 5.10 kg | 275 °F @Load 11.2 lb | ISO 306 | ||
| 165 °C @Load 1.02 kg | 329 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | as low as possible | ||||
| Emission (µgC/g) | 15 | VDA 277 | |||
| Fogging (mg) | 0.97 | 100°C;3h;DIN 75201 | |||
| 1 | 100°C;16h;DIN 75201 | ||||
| Screw Speed | low to medium | ||||