- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.905
- 拉伸强度 [MPa]: 35.0
- 热变形温度 [℃]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.49 GPa | 216 ksi | 1mm/min; ISO 527 |
| Charpy Impact, Notched | 0.450 J/cm² @Temperature 23.0 °C | 2.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-2 |
| Vicat Softening Point | 94.0 °C @Load 5.10 kg | 201 °F @Load 11.2 lb | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 - 230 °C | 374 - 446 °F | |
| Die Temperature | 200 - 230 °C | 392 - 446 °F | |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | |
| Head Temperature | 200 - 230 °C | 392 - 446 °F | |