- 熔体流动速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.905
- 弯曲模量 [MPa]: 1.65
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.65 GPa | 239 ksi | 2mm/min; ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 163 - 167 °C | 325 - 333 °F | DSC; ISO 3146 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |