- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.905
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 1.20
- 热变形温度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 - 29.0 MPa | 3920 - 4210 psi | MD/TD; ISO 527-2 |
| Elongation at Yield | 10 - 13 % | 10 - 13 % | MD/TD; ISO 527-3 |
| Tensile Modulus | 1.30 GPa | 189 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.20 GPa | 174 ksi | 5mm/min; ISO 178 |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature 23.0 °C | 2.62 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 162 - 165 °C | 324 - 329 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Optical Properties | Metric | English | Comments |
| Haze | 21 % | 21 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 20° of arc; ASTM D2457 |