- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.05
- 缺口冲击强度: 2.1
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 2.40
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Borealis Method; average process | ||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 60.0 MPa | 8700 psi | 358 N/30s; ISO 2039 | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527-2 | ||
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | ISO 527-2 | ||
| Elongation at Yield | 4.8 % | 4.8 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 2.40 GPa | 348 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 36.0 MPa | 5220 psi | at 3.5% strain; ISO 178 | ||
| 37.0 MPa | 5370 psi | at 5.5% strain; ISO 178 | |||
| Flexural Modulus | 2.40 GPa | 348 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 2.10 kJ/m² @Temperature -20.0 °C | 0.999 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | ||
| 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² @Temperature -20.0 °C | 9.99 ft-lb/in² @Temperature -4.00 °F | ISO 180/1U | ||
| 63.0 kJ/m² @Temperature 23.0 °C | 30.0 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -20.0 °C | 14.3 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.240 J/cm² @Temperature -20.0 °C | 1.14 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 58.0 µm/m-°C | 32.2 µin/in-°F | (-30°C/80°C); Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 | ||
| Vicat Softening Point | 66.0 °C @Load 5.10 kg | 151 °F @Load 11.2 lb | ISO 306 | ||
| 140 °C @Load 1.02 kg | 284 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 3.00 - 6.00 MPa | 435 - 870 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (µgC/g) | < 50 | VDA 277 | |||
| Fogging (mg) | < 2 | 100°C, 16h; DIN 75201 | |||
| Screw Speed | low to medium | ||||