Borealis RJ370MO Polypropylene, Transparent Random Copolymer

Borealis RJ370MO Polypropylene, Transparent Random Copolymer 物性表: Borealis RJ370MO Polypropylene, Transparent Random Copolymer物性表及特性介绍,Borealis RJ370MO Polypropylene, Transparent Random Copolymer注塑参数详情,如需Borealis RJ370MO Polypropylene, Transparent Random Copolymer下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 45.0
  • 密度 [g/cm3]: 0.905
  • 拉伸强度 [MPa]: 27.0
  • 硬度: 80.0
  • 热变形温度 [℃]: 73.0
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 0.905 g/cc0.0327 lb/in³ISO 1183
Linear Mold Shrinkage 0.010 - 0.020 cm/cm0.010 - 0.020 in/in
Melt Flow 45 g/10 min
@Load 2.16 kg,
Temperature 230 °C
45 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 8080ISO 2039-2
Tensile Strength, Yield 27.0 MPa3920 psi50mm/min; ISO 527-2
Elongation at Yield 13 %13 %50mm/min; ISO 527-2
Tensile Modulus 1.05 GPa152 ksi1mm/min; ISO 527-2
Charpy Impact, Notched 0.500 J/cm²
@Temperature 23.0 °C
2.38 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 73.0 °C163 °FISO 75-2
 
Optical PropertiesMetricEnglishComments
Transmission, Visible 90.0 %90.0 %transparent; thickness not quantified
 
Processing PropertiesMetricEnglishComments
Melt Temperature 210 - 260 °C410 - 500 °F
Mold Temperature 15.0 - 40.0 °C59.0 - 104 °F
Hold Pressure 20.0 - 50.0 MPa2900 - 7250 psi
 
Descriptive Properties
Injection Velocityhigh

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31689.html

免责声明: 本文 Borealis RJ370MO Polypropylene, Transparent Random Copolymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4