- 熔体流动速率 [g/10min]: 1.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 2.5 g/10 min @Load 5.00 kg, Temperature 190 °C | 2.5 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| 8.1 g/10 min @Load 5.00 kg, Temperature 230 °C | 8.1 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 80 - 100 % | 80 - 100 % | ISO 527-3 |
| Tensile Modulus | 1.10 - 1.30 GPa | 160 - 189 ksi | MD; ISO 527-3 |
| 1.20 - 1.40 GPa | 174 - 203 ksi | TD; ISO 527-3 | |
| Film Tensile Strength at Break, MD | 150 - 180 MPa | 21800 - 26100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 136 - 142 °C | 277 - 288 °F | DSC; ISO 3146 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.8 % | <= 1.8 % | ASTM D1003 |
| Gloss | >= 90 % | >= 90 % | 45° of arc; ASTM D2457 |