  4. Celanese Zenite® 6130LX WT010 LCP

Celanese Zenite® 6130LX WT010 LCP

Celanese Zenite® 6130LX WT010 LCP 物性表: Celanese Zenite® 6130LX WT010 LCP物性表及特性介绍,Celanese Zenite® 6130LX WT010 LCP注塑参数详情,如需Celanese Zenite® 6130LX WT010 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.66
  • 弯曲模量 [MPa]: 12.5
 
Physical PropertiesMetricEnglishComments
Density 1.66 g/cc0.0600 lb/in³ISO 1183
Filler Content 30 %30 %
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 145 MPa21000 psiISO 527
Elongation at Break 2.0 %2.0 %ISO 527
Tensile Modulus 15.0 GPa
@Temperature 23.0 °C		2180 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 220 MPa
@Temperature 23.0 °C		31900 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus 12.5 GPa
@Temperature 23.0 °C		1810 ksi
@Temperature 73.4 °F		ISO 178
Charpy Impact, Notched 2.00 J/cm²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 175 - 249 V175 - 249 VUL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear  -1.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		-0.556 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 23.0 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 2.00 µm/m-°C
@Thickness 2.00 mm,
Temperature -40.0 - 260 °C		1.11 µin/in-°F
@Thickness 0.0787 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 3.00 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		1.67 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		2.78 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 5.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 23.0 °C		2.78 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 6.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		3.33 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 6.00 µm/m-°C
@Thickness 4.00 mm,
Temperature -40.0 - 260 °C		3.33 µin/in-°F
@Thickness 0.157 in,
Temperature -40.0 - 500 °F		ISO 11359-1/-2
 6.00 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		3.33 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  48.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		26.7 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 2mm
 55.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		30.6 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2; 4mm
 68.0 µm/m-°C
@Temperature -40.0 - 260 °C		37.8 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 2mm
 76.0 µm/m-°C
@Temperature -40.0 - 260 °C		42.2 µin/in-°F
@Temperature -40.0 - 500 °F		ISO 11359-1/-2; 4mm
 55.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		30.6 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 62.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 23.0 - 55.0 °C		34.4 µin/in-°F
@Thickness 0.157 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 71.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 55.0 - 160 °C		39.4 µin/in-°F
@Thickness 0.0787 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 80.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 55.0 - 160 °C		44.4 µin/in-°F
@Thickness 0.157 in,
Temperature 131 - 320 °F		ISO 11359-1/-2
 80.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 160 - 260 °C		44.4 µin/in-°F
@Thickness 0.0787 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
 92.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 160 - 260 °C		51.1 µin/in-°F
@Thickness 0.157 in,
Temperature 320 - 500 °F		ISO 11359-1/-2
Melting Point 335 °C635 °F10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 280 °C536 °FISO 75-1/-2
UL RTI, Electrical  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  220 °C
@Thickness 1.50 mm		428 °F
@Thickness 0.0591 in		UL 746B
 220 °C
@Thickness 3.00 mm		428 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  240 °C
@Thickness 1.50 mm		464 °F
@Thickness 0.0591 in		UL 746B
 240 °C
@Thickness 3.00 mm		464 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		UL94
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		UL94
Glow Wire Test  960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		Glow Wire Flammability Index; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		Glow Wire Ignition Temperature; IEC 60695-2-13
 
Processing PropertiesMetricEnglishComments
Melt Temperature 355 °C671 °FOptimum
 350 - 360 °C662 - 680 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorWhite
Drying RecommendedYes
FillerGlass Reinforced
FormsPellets
GenericLCP
Part Marking Code>LCP-GF30<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
Processing MethodInjection Molding
Product CategoryElectrical Resins
 Flame Retardant Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF30ISO 1043

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31747.html

免责声明: 本文 Celanese Zenite® 6130LX WT010 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4